+ PU Casting Elastomer Prepolymer
+ PPG PU Casting Resin
+ PPG TDI PU Casting Prepolymer
+ Casting PU
+ PTMEG PU Casting Resin
+ PTMEG TDI PU Casting Prepolymer
+ PTMG PU prepolymer
+ PU Casting Prepolymer
+ Castable PU
+ PU (Polyurethane) prepolymer for casting polyurethane elastomer parts
+ Cast Polyurethane Resin
+ Castable Polyurethane
+ PU prepolymer for casting
+ PU elastomer Prepolymer
+ Casting PU Resin
+ Casting PU Prepolymer
+ Casting PU Elastomer
| Application | |||
|---|---|---|---|
| This series of hot-cast polyurethane (also named as polyurethane prepolymer) is suitable to make bushes, Castor Wheels, Couplings, Conveyor Rollers, Cutting Boards, Fork-lift Tyres, Gears, Grading Screens, Pneumatic and Oil Seals, Scrapers, Skate Wheels, Wire Guides. | |||
| Introduction | |||
|---|---|---|---|
| PTMEG-based MDI-terminated prepolymer is normally cured with1,4-Butanediol (1,4-BDO) to yield an elastomer. This product is for hot-casting polyurethane use. The product is an elastomer with excellent toughness which is characteristic of MDI-PTMEG systems without solvent or plasticizer. | |||
| PTMG + MDI hot-cast polyurethane | ||||
|---|---|---|---|---|
| CPU-MT-1080 | CPU-MT-1085 | CPU-MT-1090 | ||
| Hardness (Shore A) | 80 ± 2 | 85 ± 2 | 90 ± 2 | |
| NCO (Wt%) | 5.1 ± 0.2 | 6.3 ± 0.2 | 7.1 ± 0.2 | |
| Mixing ratio PU prepolymer : 1,4-BDO | 100 : 5 - 5.4 | 100 : 6.2 - 6.6 | 100 : 7 - 7.4 | |
| Working temperature (℃) PU prepolymer | 70 - 80 | 70 - 80 | 70 - 80 | |
| Working temperature (℃) 1,4-BDO | 25 | 25 | 25 | |
| Pot life (100g@70℃) (min) | 6 | 6 | 4 | |
| Tensile strength (Kgf/cm2) | 235 ± 25 | 400 ± 40 | 440 ± 40 | |
| Elongation (%) | 550 ± 50 | 500 ± 50 | 480 ± 50 | |
| Tear Strength (Kgf/cm) | 70 ± 5 | 85 ± 5 | 100 - 115 | |
| Processing procedure | 1) Pour mixed materials into moulds, which have been preheated to 110℃ and precoated with release agent. Demold casting after 2 hours at 110℃. 2) The casting should be post-cured at 110℃ for 16 hours. | 1) Pour mixed materials into moulds, which have been preheated to 110℃ and precoated with release agent. Demold casting after 1 hour at 110℃. 2) The casting should be post-cured at 110℃ for 16 hours. | 1) Pour mixed materials into moulds, which have been preheated to 110℃ and precoated with release agent. Demold casting after 1 hour at 110℃. 2) The casting should be post-cured at 110℃ for 16 hours. | |
| Notice: These values are based on the test of our present laboratory test specimens. | ||||
| Storage | |||
|---|---|---|---|
| To avoid moisture in the air, hot-cast polyurethane should be stored in sealed container at room temperature. Avoid direct sunlight exposure. | |||
| Shelf life | |||
|---|---|---|---|
| 6 months. | |||
| Packing | |||
|---|---|---|---|
| 200 kgs/drum. | |||
Taiwan PU Corporation is a professional hot-cast polyurethane manufacturer, hot-cast polyurethane producer. We supply high quality hot-cast polyurethane products, have an experienced technical team and offer the best price to hot-cast polyurethane.
Hot-cast polyurethane is called hot cast PU, hot cast PU material, hot cast polyurethane material, MDI terminated hot cast polyurethane, PTMG MDI hot cast polyurethane, MDI terminated hot cast PU, MDI terminated hot cast PU material, MDI hot cast PU, hot cast polyurethane system, hot cast polyurethane resin, hot cast PU resin, hot cast PU system, hot cast polyurethane raw material, hot cast PU raw material. If hot-cast polyurethane is needed, please contact us.