Application | |||
---|---|---|---|
Printing coating agents, adhesive tackifier, printing ink, paint, synthetic leather and PVC leather to enhance the adhesive viscosity. |
Introduction | |||
---|---|---|---|
Though chloroprene rubber has an excellent weathering, oil and chemical resistance, it is necessary, in practice, to make use of a modifying agent to improve the properties of chloroprene rubber adhesive, such as tackiness retention time, phasing stability, heat resistance and adhesion strength. Alkyl phenolic resin "APU-20-52G" is excellently compatible with chloroprene rubber and an indispensable modifying agent for chloroprene rubber for manufacturing adhesive to meet specific purposes. |
Alkyl phenolic resin |
---|
1) Specifications | |||
ITEM NO. | Appearance | MgO Reactivity (%) | Softening point (℃, R&B) |
APU-20-52G | Pale yellow, lump | 6.5 | 115-130 |
2) Typical Formulation (MgO Prereation) | |
Part 1 | Parts by wt. |
Chloroprene TA-50 | 100 |
MgO | 4 |
ZnO | 5 |
Stabilizer | 2 |
Part 2 | Parts by wt. |
APU-20-52G | 50 |
Toluene | 150 |
MgO | 5 |
Water | 0.5 |
Part 3 | Parts by wt. |
Toluene | 96 |
n-Hexane | 123 |
Ethyl acetate | 123 |
(Solvent formula in total : Toluene/n-Hexane/Ethyl acetate = 2/1/1) Procedure Mix ingredients of Part 1 together on milling roll then dissolve in mixed solvent (Part 3). Stir Part 2 in a vessel for 5 hours, then add it the mixture of Part 1 and Part 3. Keep agitation further 5 hours to give adhesive of 25% solids. |
3) Adhesive Properties | ||||||
ITEM NO. | Adhesion Strength | Tackiness Retention | Heat Resistance | Phasing Resistance | ||
After 5 hours | After 24 hours | At 60℃ | ||||
APU-20-52G | B | B | B | B | B | B |
A: Excellent B: Good C: Fair X: Poor |
a) Heat Resistance | ||
ITEM NO. | Heat Resistance (℃) | Result |
APU-20-52G | 84 | B |
Test Conditions | |
Method | ASTM-D-816-55 |
Weight | 500g |
Adherend | Steel to vulcanized rubber |
Test Conditions | Kept 3 days after bonding |
Temperature graduation | 2℃/5 min |
b) Phasing Resisttance Adhesives in stoppered jar were kept for one month at 20℃ then phasing was observed | |
Excellent | Completely no phasing |
Good | Top part is slightly phasing |
Fair | 5% of upper part is phasing |
Poor | 50% of adhesive is phasing |
c) Tackiness Retention Time | ||
ITEM NO. | Tackiness Retention Time | Result |
APU-20-52G | 10 min, 15 sec. | B |
d) Adhesion Strength Test Conditions | |
Peeling angle | 180° |
Adhesion strength at 60℃ | Test pieces were kept 3 days after bonding then kept one hour at 60℃ before test. |
Adherend | Steel to canvas |
Peeling velocity | 200 mm/min |
Temperature | 20℃ (68℉) |
ITEM NO. | Elapsed Days | At 60℃ | Initial Strength | |||||
1 | 3 | 7 | Result | 1 hour | Result | 5 hour | Result | |
APU-20-52G | 4.8 | 11.6 | 14.5 | B | 6.4 | B | 2.5 | B |
Unit : kg/25 mm |
e) Shear strength | |
Shearing velocity | 50 mm/min |
Glued area | 10 mm x 25 mm |
Test Conditions | at 20℃ (68℉) |
Open time | 10 min |
Bonded material | Plywood to plywood |
ITEM NO. | Elapsed Days | Result | ||
1 | 3 | 7 | ||
APU-20-52G | 22.2 | 32.8 | 43.0 | B |
Unit : kg/25 mm2 |
Taiwan PU Corporation is a professional alkyl phenolic resin manufacturer, alkyl phenolic resin producer. We supply high quality alkyl phenolic resin products, have an experienced technical team and offer the best price to alkyl phenolic resin.
Alkyl phenolic resin is called phenol formaldehyde resin for adhesive, phenolic resin for adhesive, phenolic resin tackifier for adhesive. If alkyl phenolic resin is needed, please contact us.
****We cordially invite you to access our following website to know more about our Phenolic Resin - https://www.taiwanpu.com/en/product/Phenolic-resin/Alkyl-phenolic-resin?page=1&rtnKind=Phenolic-resin
Taiwantrade.com and iDealEZ.com uses analytical cookies and other tracking technologies to offer you the best possible user experience. By using our website, you acknowledge and agree to our cookie policy.
For more information on cookies or changing your cookies settings, read Taiwantrade & iDealEZ’s Privacy Policy.