Liquid MOCA

MOCA - E300 (LIQUID)

+ Liquid MOCA

+ Hardener for casting PU

+ Curing Agent for polyurethane

+ DMTDA AMBER LIQUID INSTEAD OF MOCA

+ Polyurethane Curing Agent

+ Liquid MOCA DMTDA

DMTDA E300

Key features：
- Appearance: amber liquid
- Good replacement for MOCA
- Non toxic to human being
- No need to preheat
- Eco-friendly

Application
PU coatings, architectural coatings, sports materials, epoxy insulation material, waterproof wall and waterproof roofing materials. Printing rollers, rollers, trolley wheels and molds of PU elastomers.

Introduction
MOCA is used as PU (Polyurethane Resin) curing agent. The chlorine atoms on benzene ring can slow down the activity of "NH2" group, so as to extend the pot life while casting.

Structural Formula

Physical Properties of DMTDA E300 Curative
Equivalent Weight				107
Appearance				Amber Liquid
Odor				Slight Amin
Boiling Point,℉(℃)				667(353)(decomposes)
Density(g/cm³) @68℉(20℃)				1.21
Density(g/cm³) @140℉(60℃)				1.18
Density(g/cm³) @212℉(100℃)				1.15
Viscosity, Cps @68℉(20℃)				690
Viscosity, Cps @140℉(60℃)				22
Viscosity, Cps @212℉(100℃)				5
Vapor Pressure, mm @65℉(20℃)				0.6
Amine Number, mg.KOH/g				536
TDA content %, by weight				≤1.0%
Moisture				≤0.1%

Processing
DMTDA E300, being a liquid at room temperature result in significant processing advantages, for example, in such operation as transfer, melting down of solids is eliminated. Also, the possibility of freezing-up is no longer a concern during mixing or in meter mixing machines. Additionally, its liquid state permits processing prepolymer at lower temperatures than that of MOCA. DMTDA E300 has an equivalent weight of 107 compared to 133.5 for MOCA. This means that about 20% less by weight is required for a given prepolymer at the same stoichiometry.

Example
Prepolymer (% NCO 4.1)	100Pts	100Pts
MOCA @ 95% Theory	12.4Pts	-
DMTDA E300 @ 95% Theory	-	9.9Pts
Formula Weight	112.4Pts	109.9Pts
The specific gravity of DMTDA E300 is about 1.2g/cm³ at recommended use temperatures of 70-90℉(21-33℃) ,whereas the specific gravity of molten MOCA at its use temperature of molten MOCA at its use temperature of 240℉(116℃) is 1.26. This means that weight delivery by volumetric pimps is comparable for the two materials and therefore if no alterations for meter-mixing machines, we must change the formula weight of MOCA into that of DMTDA E300.

Physical Properties of Prepolymer Cured With DMTDA E300 Curative
The physical properties of prepolymer, both ether and ester types, when cured with DMTDA E300 curative, are comparable to those obtained with MOCA. As in MOCA-curing system, physical properties are sensitive to the ration (stoichiomety) of curative to prepolymer. DMTDA E300 curative exhibition tolerance to stoichiomety variations similar to that of MOCA. Low stoichiomety (80~90%) generally tends to maximize properties such as compression set resistance, while high stoichiomety (100-105%) tends to maximize properties such as tear strength and flex life. The best results for most application are obtained at about 95% stoichiometry. While cure conditions (temperature and times) are similar to those used with MOCA, DMTDA E300 curative requires somewhat closer attention to post cure conditions to obtain maximum physical properties, particularly with respect to compression set and dynamic properties. Use the recommended schedules listed.

Package
20kg per iron drum or 200kg per iron drum Notice: These values are based on the test of our present laboratory test specimens.

Taiwan PU Corporation is a professional DMTDA E300 manufacturer, DMTDA E300 producer. We supply high quality DMTDA E300 products, have an experienced technical team and offer the best price to DMTDA E300.

DMTDA E300 is called liquid MOCA, DMTDA for prepolymer, DMTDA curative, DMTDA curing agent, DMTDA for polyurethane elastomer, MOCA substitute, eco-friendly substitute of MOCA. If DMTDA is needed, please contact us.

Liquid MOCA

DMTDA E300